Pore size effects on the sorption of supercritical carbon dioxide in mesoporous CPG-10 silica
- ORNL
- Helmholtz-Zentrum Berlin
- Ohio State University
Excess sorption isotherms of supercritical carbon dioxide in mesoporous CPG-10 silica glasses with nominal pore sizes of 75 (7.5 nm) and 350 (35 nm) were measured gravimetrically at 35 C and 50 C and pressures of 0-200 bar. Formation of broad maxima in the excess sorption was observed at fluid densities below the bulk critical density. Positive values of excess sorption were measured at bulk densities below about 0.65-0.7 g/cm3, whereas zero and negative values were obtained at higher densities, indicating that the interfacial fluid becomes less dense than the corresponding bulk fluid at high fluid densities. A shift of the excess sorption peak position to higher fluid density is found with increasing pore width. The excess sorption of CO2 normalized to the specific surface area is higher for the 35 nm pore size material, suggesting pore confinement effects. Conversely, the pore volume normalized excess sorption is higher for the 7.5 nm pore size material. Assessment of mean pore density reveals regions of constant pore fluid density, located between the excess sorption peak and the adsorption/depletion transition. Both materials exhibit such regions of constant mean pore fluid density as a function of bulk CO2 density at the lower temperature of 35 C, but not at 50 C. The results of this study suggest that the CO2 storage capacity in quartz-rich reservoirs is higher for sites with low temperature and rock textures characterized by narrow pores with high surface to volume ratios.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1033158
- Journal Information:
- Journal of Physical Chemistry C, Vol. 116, Issue 1; ISSN 1932-7447
- Country of Publication:
- United States
- Language:
- English
Similar Records
CO2 Adsorption to Sub-Single Hydration Layer Montmorillonite Clay Studied by Excess Sorption and Neutron Diffraction
Adsorption and Depletion Regimes of a Nonionic Surfactant in Hydrophilic Mesopores: An Experimental and Simulation Study