XeF2 vapor phase silicon etch used in the fabrication of movable SOI structures.
Vapor phase XeF{sub 2} has been used in the fabrication of various types of devices including MEMS, resonators, RF switches, and micro-fluidics, and for wafer level packaging. In this presentation we demonstrate the use of XeF{sub 2} Si etch in conjunction with deep reactive ion etch (DRIE) to release single crystal Si structures on Silicon On Insulator (SOI) wafers. XeF{sub 2} vapor phase etching is conducive to the release of movable SOI structures due to the isotropy of the etch, the high etch selectivity to silicon dioxide (SiO{sub 2}) and fluorocarbon (FC) polymer etch masks, and the ability to undercut large structures at high rates. Also, since XeF{sub 2} etching is a vapor phase process, stiction problems often associated with wet chemical release processes are avoided. Monolithic single crystal Si features were fabricated by etching continuous trenches in the device layer of an SOI wafer using a DRIE process optimized to stop on the buried SiO{sub 2}. The buried SiO{sub 2} was then etched to handle Si using an anisotropic plasma etch process. The sidewalls of the device Si features were then protected with a conformal passivation layer of either FC polymer or SiO{sub 2}. FC polymer was deposited from C4F8 gas precursor in an inductively coupled plasma reactor, and SiO{sub 2} was deposited by plasma enhanced chemical vapor deposition (PECVD). A relatively high ion energy, directional reactive ion etch (RIE) plasma was used to remove the passivation film on surfaces normal to the direction of the ions while leaving the sidewall passivation intact. After the bottom of the trench was cleared to the underlying Si handle wafer, XeF{sub 2} was used to isotropically etch the handle Si, thus undercutting and releasing the features patterned in the device Si layer. The released device Si structures were not etched by the XeF{sub 2} due to protection from the top SiO{sub 2} mask, sidewall passivation, and the buried SiO{sub 2} layer. Optimization of the XeF{sub 2} process and the sidewall passivation layers will be discussed. The advantages of releasing SOI devices with XeF{sub 2} include avoiding stiction, maintaining the integrity of the buried SiO{sub 2}, and simplifying the fabrication flow for thermally actuated devices.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 1026980
- Report Number(s):
- SAND2010-7005C; TRN: US201121%%191
- Resource Relation:
- Conference: Proposed for presentation at the AVS 57th International Symposium & Exhibition held October 18-22, 2010 in Albuquerque, NM.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Impact of carrier wafer on etch rate, selectivity, morphology, and passivation during GaN plasma etching
Tandem Microwire Solar Cells for Flexible High Efficiency Low Cost Photovoltaics