Title: Carbon Fiber Composites for Harsh Nuclear Environments

Abstract

No abstract prepared.

Authors:
 [1];  [1];  [1];  [2]
  1. ORNL
  2. Idaho National Laboratory (INL)
Publication Date:
Research Org.:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Sponsoring Org.:
USDOE Office of Nuclear Energy (NE)
OSTI Identifier:
1023812
DOE Contract Number:
DE-AC05-00OR22725
Resource Type:
Journal Article
Resource Relation:
Journal Name: Fusion Science and Technology; Journal Volume: 94; Journal Issue: 1
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CARBON FIBERS; COMPOSITE MATERIALS; ORNL

Citation Formats

Snead, Lance Lewis, Klett, James William, Katoh, Yutai, and Windes, Will. Carbon Fiber Composites for Harsh Nuclear Environments. United States: N. p., 2006. Web.
Snead, Lance Lewis, Klett, James William, Katoh, Yutai, & Windes, Will. Carbon Fiber Composites for Harsh Nuclear Environments. United States.
Snead, Lance Lewis, Klett, James William, Katoh, Yutai, and Windes, Will. Sun . "Carbon Fiber Composites for Harsh Nuclear Environments". United States. doi:.
@article{osti_1023812,
title = {Carbon Fiber Composites for Harsh Nuclear Environments},
author = {Snead, Lance Lewis and Klett, James William and Katoh, Yutai and Windes, Will},
abstractNote = {No abstract prepared.},
doi = {},
journal = {Fusion Science and Technology},
number = 1,
volume = 94,
place = {United States},
year = {Sun Jan 01 00:00:00 EST 2006},
month = {Sun Jan 01 00:00:00 EST 2006}
}
  • The mechanical performance of carbon-fiber matrix composites with different fiber architectures is investigated for various loading modes. All the composites were fabricated from nominally equal constituents and identical consolidation processes, leaving as the only variables, the variations caused by the different fiber weave structures. The fiber architecture drastically affects both composite strength and deformation characteristics. Some systems are almost linear up to a final brittle failure while others exhibit a pronounced non-linearity prior to failure. It is found that the composite tensile strength is dictated by both fiber volume and fraction and weave architecture. The weaving can have a beneficialmore » effect in spite of introducing new fiber flaws and stress concentrations, because it causes the composite to be less flaw sensitive. These features are addressed analytically by considering the statistical aspects of the fiber strength and the formation of critical defects.« less
  • Silicon carbide composites are attractive for structural applications in fusion energy systems because of their low activation and afterheat properties, excellent high-temperature properties, corrosion resistance, and low density. These composites are relatively new materials with a limited database; however, there is sufficient understanding of their performance to identify key issues in their application. To date, dimensional changes of the constituents, microstructural evolution, radiation-enhanced creep, and slow crack growth have been identified as potential lifetime limiting mechanisms. Experimental evidence of these mechanisms, the factors that control them, and their implications on component lifetime will be discussed.
  • Carbon fiber-reinforced epoxy matrix composites, with a tensile fracture stress of either 3.5 or 5.5GPa (designated as 3.5 and 5.5GPa CF/RE composites, respectively), were studied to determine the effect of fiber strength on the tensile fracture behavior. The smooth and notched tensile specimens were loaded in the direction parallel to the fibers. The 5.5GPa CF/RE composite exhibited a higher smooth tensile fracture stress but a significantly decreased notch strength ratio compared with the 3.5GPa CF/RE composite. For the smooth tensile specimens of the 3.5GPa CF/RE composite, a zigzag fracture approximately perpendicular to the loading direction occurred, and the fracture processmore » involved a brittle fracture, or pull out, of the fibers; whereas, for the 5.5GPa CF/RE composite, the fracture was approximately parallel to the loading direction, and fiber-matrix interfacial fracture was observed. For the notch tensile tests, fracture occurred at the fiber-matrix interfaces independent of the composite type. The results are described and discussed.« less
  • Interfacial mechanical properties of carbon-coated-S-glass-fiber-reinforced cement were characterized by a fiber pushout technique. The pushout experiments were conducted on model composites, where the S-glass monofilaments with and without carbon coating were unidirectionally embedded in ordinary portland cement. Interfacial properties, including bonding strength, frictional stress, residual stress, and fracture energy, were extracted from the previously developed progressive debonding model. The composite with a carbon interface exhibited a weaker interfacial bonding strength and frictional stress than did the composite without a carbon interface. The interfacial fracture energy of the composite with a carbon interface was 7.9 J/m{sup 2}, as compared to 47.6more » J/m{sup 2} for the composite without a carbon interface. The composite with the carbon interface exhibited a smaller residual clamping stress (18 MPa), in comparison to that for the composite without a carbon interface (69 MPa). Scanning electron microscopy observations indicated that the filament without a carbon coating was significantly attacked by the alkaline environment and was strongly bonded onto the matrix, whereas the filament with a carbon coating remained intact under the same curing conditions. These studies suggest that carbon coating provides the glass fiber with significantly improved corrosion resistance to alkali in the cement environment.« less
  • The authors studied covalent grafting to functionalized carbon fibers of a specially designed liquid crystalline monomer and its corresponding side-chain liquid crystalline polymer containing pendant chemical functions on their mesogenic groups. From a materials point of view these liquid crystalline compounds could act as coupling agents at fiber/polymer matrix interfaces, offering a mechanism to control composite properties not only through bonding but also through their [open quotes]spontaneous[close quotes] molecular orientation in interfacial regions. The grafting methodology for both monomer and polymer to fiber surfaces involved esterification through carbodiimide chemistry in solution. Carboxylic acid groups found on functionalized carbon fiber surfacesmore » were esterified to phenolic functions in the side chains of the experimental polymer. Following grafting procedures the fibers were analyzed by scanning electron microscopy (SEM) and by contact angle measurements. SEM micrographs of fibers grafted with polymer revealed the presence of strongly attached polymeric material on the graphitic surface after rigorous extraction with polymer solvent. Contact angle measurements and polar/dispersive free energy analysis indicated also a smaller polar component of the surface free energy of fibers possibly due to the hydrophobic polymer backbone grafted on the carbon surfaces. On the basis of results, it is concluded that the esterification reaction grafted the polyphenolic liquid-crystal polymer on graphite fiber surfaces. 24 refs., 8 figs., 4 tabs.« less