Effects of neutron irradiation and hydrogen on ductile-brittle transition temperatures of V-Cr-Ti alloys
The effects of neutron irradiation and hydrogen on the ductile- brittle transition temperatures (DBTTs) of unalloyed vanadium and V-Cr-Ti alloys were determined from Charpy-impact tests on 1/3 ASTM standard size specimens and from impact tests on 3-mm diameter discs. The tests were conducted on specimens containing <30 appm hydrogen and 600-1200 appm hydrogen and on specimens after neutron irradiation to 28-46 dpa at 420, 520, and 600C. The DBTTs were minimum (< {minus}220{degree}C) for V-(105)Ti alloys under for V-4-Cr-4Ti alloy with <30 appm hydrogen. The effect of 600-1200 appm hydrogen in the specimens was to raise the DBTTs by 100--150{degree}C. The DBTTs were minimum (< {minus}220{degree}C) for V-(1-5)Ti alloys and V-4-Cr-4Ti alloys after neutron irradiation.
- Research Organization:
- Argonne National Lab., IL (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 10189298
- Report Number(s):
- ANL/ET/CP-80889; CONF-930928-8; ON: DE94001466; TRN: 93:024109
- Resource Relation:
- Conference: 6. international conference on fusion reactor materials,Stresa (Italy),27 Sep - 1 Oct 1993; Other Information: PBD: Aug 1993
- Country of Publication:
- United States
- Language:
- English
Similar Records
Response of unirradiated and neutron-irradiated vanadium alloys to Charpy-impact loading
Effect of dynamically charged helium on mechanical properties of V-4Cr-4Ti
Related Subjects
36 MATERIALS SCIENCE
THERMONUCLEAR REACTOR MATERIALS
DUCTILE-BRITTLE TRANSITIONS
PHYSICAL RADIATION EFFECTS
VANADIUM BASE ALLOYS
DAMAGING NEUTRON FLUENCE
VANADIUM
HYDROGEN EMBRITTLEMENT
TRANSITION TEMPERATURE
CHROMIUM ALLOYS
TITANIUM ALLOYS
TEMPERATURE DEPENDENCE
700480
360106
COMPONENT DEVELOPMENT
MATERIALS STUDIES
RADIATION EFFECTS