High-Density Plasma Arc Heating Studies of FePt Thin Films
Journal Article
·
· Journal of the Minerals Metals & Materials Society (JOM)
- ORNL
- University of Alabama, Tuscaloosa
The effect of pulsed-thermal-processing with high-density plasma arc heating is discussed for 20 nm thick nanocrystalline FePt thin films. The dependence of the A1 {yields} L1{sub 0} phase transformation on pulsed time and radiant energy of the pulse is quantified through x-ray diffraction and alternating gradient magnetometry. For 100 ms and 250 ms pulse widths, the phase transformation was observed. Higher radiant energy densities resulted in a larger measured coercivity associated with the L1{sub 0} phase.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Laboratory Directed Research and Development (LDRD) Program
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1003509
- Journal Information:
- Journal of the Minerals Metals & Materials Society (JOM), Vol. 58, Issue 6; ISSN 1047-4838
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermal annealing of FePt thin films by millisecond plasma arc pulses
Pulsed-Thermal-Processing of Chemically Synthesized FePt Nanoparticles
On the relationship of high coercivity and L1{sub 0} ordered phase in CoPt and FePt thin films
Journal Article
·
Thu Jan 01 00:00:00 EST 2009
· Journal of Magnetism and Magnetic Materials
·
OSTI ID:1003509
+4 more
Pulsed-Thermal-Processing of Chemically Synthesized FePt Nanoparticles
Journal Article
·
Sun Jan 01 00:00:00 EST 2006
· Journal of the Minerals Metals & Materials Society (JOM)
·
OSTI ID:1003509
+5 more
On the relationship of high coercivity and L1{sub 0} ordered phase in CoPt and FePt thin films
Journal Article
·
Fri Oct 01 00:00:00 EDT 1999
· Journal of Applied Physics
·
OSTI ID:1003509
+2 more