High Temperature Fracture Characteristics of a Nanostructured Ferritic Alloy (NFA)
Journal Article
·
· Journal of Nuclear Materials
- ORNL
- Korea Atomic Energy Research Institute
High temperature fracture behavior has been investigated for the nanostructured ferritic alloy 14YWT (SM10). The fracture toughness of the alloy was above 140 MPa m at low temperatures, room temperature (RT) and 200 C, but decreased to a low fracture toughness range of 52 82 MPa m at higher temperatures up to 700 C. This behavior was explained by the fractography results indicating that the unique nanostructure of 14YWT alloy produced shallow plasticity layers at high temperatures and a low-ductility grain boundary debonding occurred at 700 C.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1000297
- Journal Information:
- Journal of Nuclear Materials, Vol. 407, Issue 12; ISSN 0022-3115
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile fracture characteristics of nanostructured ferritic alloy 14YWT
Fracture toughness evaluation of select advanced replacement alloys for LWR core internals
Effects of Partial Phase Transformation on Characteristics of 9Cr Nanostructured Ferritic Alloy
Journal Article
·
Fri Jan 01 00:00:00 EST 2010
· Journal of Nuclear Materials
·
OSTI ID:1000297
Fracture toughness evaluation of select advanced replacement alloys for LWR core internals
Technical Report
·
Tue Aug 01 00:00:00 EDT 2017
·
OSTI ID:1000297
Effects of Partial Phase Transformation on Characteristics of 9Cr Nanostructured Ferritic Alloy
Journal Article
·
Wed Jan 01 00:00:00 EST 2014
· Current Nanoscience
·
OSTI ID:1000297