A Theory for the RF Surface Field for Various Metals at the Destructive Breakdown Limit
By destructive breakdown we mean a breakdown event that results in surface melting over a macroscopic area in a high E-field region of an accelerator structure. A plasma forms over the molten area, bombarding the surface with an intense ion current ({approx} 10{sup 8} A/cm{sup 2}), equivalent to a pressure of about a thousand Atmospheres. This pressure in turn causes molten copper to migrate away from the iris tip, resulting in measurable changes in the iris shape. The breakdown process can be roughly divided into four stages: (1) the formation of ''plasma spots'' at field emission sites, each spot leaving a crater-like footprint; (2) crater clustering, and the formation of areas with hundreds of overlapping craters; (3) surface melting in the region of a crater cluster; (4) the process after surface melting that leads to destructive breakdown. The physics underlying each of these stages is developed, and a comparison is made between the theory and experimental evidence whenever possible. The key to preventing breakdown lies in stage (3). A single plasma spot emits a current of several amperes, a portion of which returns to impact the surrounding area with a power density on the order 10{sup 7} Watt/cm{sup 2}. This power density is not quite adequate to melt the surrounding surface on a time scale short compared to the rf pulse length. In a crater field, however, the impact areas from multiple plasma spots overlap to provide sufficient power density for surface melting over an area on the order of 0.1 mm{sup 2} or more. The key to preventing breakdown is to choose an iris tip material that requires the highest power density (proportional to the square of the rf surface field) for surface melting, taking into account the penetration depth of the impacting electrons. The rf surface field required for surface melting (relative to copper) has been calculated for a large number elementary metals, plus stainless-steel and carbon.
- Research Organization:
- SLAC National Accelerator Lab., Menlo Park, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC02-76SF00515
- OSTI ID:
- 900599
- Report Number(s):
- SLAC-PUB-12354; TRN: US0702417
- Journal Information:
- AIP Conf.Proc.877:27-40,2006, Conference: Invited tutorial presented at 12th Advanced Accelerator Concepts Workshop (AAC 2006), Lake Geneva, Wisconsin, 10-15 Jul 2006
- Country of Publication:
- United States
- Language:
- English
Similar Records
A Theory for the Comparative RF Surface Fields at Destructive Breakdown for Various Metels
Gradient limitation in accelerating structures imposed by surface melting