Friction and wear performance of low-friction carbon coatings under oil lubrication.
Amorphous carbon coatings with very low friction properties were recently developed at Argonne National Laboratory. These coatings have shown good promise in mitigating excessive wear and scuffing problems associated with low-lubricity diesel fuels. To reduce the negative effect of sulfur and other lubricant additives in poisoning the after-treatment catalyst, a lubricant formulation with a low level of sulfur may be needed. Exclusion of proven sulfur-containing extreme pressure (EP) and antiwear additives from oils will require other measures to ensure durability of critical lubricated components. The low-friction carbon coating has the potential for such applications. In the present study, we evaluated the friction and wear attributes of three variations of the coating under a boundary lubrication regime. Tests were conducted with both synthetic and mineral oil lubricants using a ball-on-flat contact configuration in reciprocating sliding. Although the three variations of the coating provided modest reductions in friction coefficient, they all reduced wear substantially compared to an uncoated surface. The degradation mode of oxidative wear on the uncoated surface was replaced by a polishing wear mode on the coated surfaces.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31-109-ENG-38
- OSTI ID:
- 795815
- Report Number(s):
- ANL/ET/CP-105672; TRN: US200214%%709
- Resource Relation:
- Journal Volume: 1; Conference: 2002 Future Car Congress, Arlington, VA (US), 06/03/2002--06/05/2002; Other Information: PBD: 11 Dec 2001
- Country of Publication:
- United States
- Language:
- English
Similar Records
Large-scale Manufacturing of Nanoparticulate-based Lubrication Additives for Improved Energy Efficiency and Reduced Emissions
Scuffing performance of amorphous carbon during dry-sliding contact.