Study of Caustic Corrosion of Carbon Steel Waste Tanks
Solution chemistry of wastes from US atomic weapons production is controlled to inhibit corrosion of carbon steel tanks used in containment and storage. The pH, nitrate ion and nitrite ion concentrations of fresh solutions are maintained within specified limits for this purpose. In the start up process for a new waste evaporator (RHL WE), non-radioactive solutions of similar chemistry will be circulated through carbon steel piping between a steel tank and the evaporator. The evaporator is fabricated from a corrosion resistant nickel base alloy. The equipment will be exposed continuously to the hot corrosive caustic solutions. Published corrosion rates for steel in pure caustic at the elevated temperatures indicate losses >1.3 mm/y. Because the total test period for start up is relatively short, penetration will not occur. However, concern exists because the rust particles will probably circulate and precipitate throughout the system.A laboratory study was performed in order to determine corrosion to be expected for the specific waste solutions being used in start up testing of the new equipment. In summary, the test results indicate that the corrosion rates for steel are acceptable for the short term simulant tests for the new evaporator. The amount of particulate is probably not a concern, through filtration is recommended as an option. the hydrogen formation is also not a concern because it is in a steam environment, and is continuously swept from the storage vessel.
- Research Organization:
- Savannah River Site (SRS), Aiken, SC (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC09-96SR18500
- OSTI ID:
- 4823
- Report Number(s):
- WSRC-MS-99-00055; ON: DE00004823
- Resource Relation:
- Conference: 14th International Corrosion Congress, Cape Town, (S. Africa), 26-1 Sep 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Waste Treatment Technology Process Development Plan For Hanford Waste Treatment Plant Low Activity Waste Recycle
INVESTIGATION OF THE POTENTIAL FOR CAUSTIC STRESS CORROSION CRACKING OF A537 CARBON STEEL NUCLEAR WASTE TANKS