Solar-thermal Water Splitting Using the Sodium Manganese Oxide Process & Preliminary H2A Analysis
There are three primary reactions in the sodium manganese oxide high temperature water splitting cycle. In the first reaction, Mn2O3 is decomposed to MnO at 1,500°C and 50 psig. This reaction occurs in a high temperature solar reactor and has a heat of reaction of 173,212 J/mol. Hydrogen is produced in the next step of this cycle. This step occurs at 700°C and 1 atm in the presence of sodium hydroxide. Finally, water is added in the hydrolysis step, which removes NaOH and regenerates the original reactant, Mn2O3. The high temperature solar-driven step for decomposing Mn2O3 to MnO can be carried out to high conversion without major complication in an inert environment. The second step to produce H2 in the presence of sodium hydroxide is also straightforward and can be completed. The third step, the low temperature step to recover the sodium hydroxide is the most difficult. The amount of energy required to essentially distill water to recover sodium hydroxide is prohibitive and too costly. Methods must be found for lower cost recovery. This report provides information on the use of ZnO as an additive to improve the recovery of sodium hydroxide.
- Research Organization:
- University of Colorado
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FG36-05GO15044
- OSTI ID:
- 1053709
- Report Number(s):
- DOE/05GO15044
- Country of Publication:
- United States
- Language:
- English
Similar Records
Acid-base model for thermochemical water splitting: results of experimental tests on manganese-based thermochemical cycles
Development of Alkaline Oxidative Dissolution Methods for Chromium (III) Compounds Present in Hanford Site Tank Sludges