Radiation Effect on Microstructural Stability of RERTR Fuel
Conference
·
OSTI ID:927630
Three depleted uranium alloys are successfully cast for the radiation stability studies of the fuel-cladding interaction product using proton irradiation. SEM analysis indicates the presence of the phases of interest: U(Si,Al)3, (U,Mo)(Si,Al)3 and a mixture of UMo2Al20, U6Mo4Al43, and UAl4. Irradiation with 2.6 MeV protons at 200ºC to the doses of 0.1, 1.0 and 3.0 dpa are carried out.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- DOE - NE
- DOE Contract Number:
- DE-AC07-99ID-13727
- OSTI ID:
- 927630
- Report Number(s):
- INL/CON-08-13804; TRN: US0804803
- Resource Relation:
- Conference: 12th Annual Topical Meeting on Research Reactor Fuel Management (RRFM),Hamburg, Germany,03/02/2008,03/05/2008
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure Characterization of RERTR Fuel
Kr Ion Irradiation Study of the Depleted-Uranium Alloys
Microstructure of RERTR Du-Alloys Irradiated with Krypton Ions up to 100 dpa
Conference
·
Mon Sep 01 00:00:00 EDT 2008
·
OSTI ID:927630
+2 more
Kr Ion Irradiation Study of the Depleted-Uranium Alloys
Journal Article
·
Wed Dec 01 00:00:00 EST 2010
· Journal of Nuclear Materials
·
OSTI ID:927630
+4 more
Microstructure of RERTR Du-Alloys Irradiated with Krypton Ions up to 100 dpa
Journal Article
·
Fri Apr 01 00:00:00 EDT 2011
· Journal of Nuclear Materials
·
OSTI ID:927630
+4 more