Isothermal Martensitic and Pressure-Induced ? to ?? Phase Transformations in a Pu-Ga Alloy
A Pu-2 at.% Ga alloy specimen is slowly compressed to {approx}1 GPa in a large volume moissanite anvil cell to induce the face-centered cubic {delta} to simple monoclinic {alpha}{prime} phase transformation. Optical microscopy, x-ray diffraction, and transmission electron microscopy of the specimen recovered to ambient pressure reveal that the vast majority of the microstructure consists of the {alpha}{prime} phase with grain sizes ranging from 10 nm to several hundred nm, with the remainder being {delta} phase dispersed between the {alpha}{prime} grains. This morphology is in contrast to the transformation product of the low-temperature isothermal martensite in which the lath-shaped {alpha}{prime} particles are {approx}20 {micro}m by 2 {micro}m.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 925680
- Report Number(s):
- UCRL-CONF-234546; TRN: US200810%%82
- Resource Relation:
- Conference: Presented at: Plasticity 2008, Kailua/Kona, HI, United States, Jan 03 - Jan 08, 2008
- Country of Publication:
- United States
- Language:
- English
Similar Records
Orientation relationship, plasticity, twin relationship, and interfacial structure of the ???' isothermal martensitic transformation in Pu-Ga alloys
Probing the isothermal (delta)->(alpha)' martensitic transformation in Pu-Ga with in situ x-ray diffraction