A comprehensive matrix of 60 tests was designed to explore the effect of calcium chloride vs. sodium chloride and the ratio R of nitrate concentration over chloride concentration on the repassivation potential of Alloy 22. Tests were conducted using the cyclic potentiodynamic polarization (CPP) technique at 75 C and at 90 C. Results show that at a ratio R of 0.18 and higher nitrate was able to inhibit the crevice corrosion in Alloy 22 induced by chloride. Current results fail to show in a consistent way a different effect on the repassivation potential of Alloy 22 for calcium chloride solutions than for sodium chloride solutions.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 924597
- Report Number(s):
- UCRL-CONF-233678; TRN: US200809%%384
- Resource Relation:
- Conference: Presented at: IEEE Pulsed Power and Plasma Science Conference, Albuquerque, NM, United States, Jun 17 - Jun 22, 2007
- Country of Publication:
- United States
- Language:
- English
Similar Records
Repassivation Potential of Alloy 22 in Sodium and Calcium Chloride Brines
Localized Corrosion of Alloy 22 -Fabrication Effects-
Localized Corrosion of Alloy 22 -Fabrication Effects-FY05 Summary Report
Conference
·
Sat Aug 11 00:00:00 EDT 2007
·
OSTI ID:924597
Localized Corrosion of Alloy 22 -Fabrication Effects-
Technical Report
·
Sat Nov 05 00:00:00 EST 2005
·
OSTI ID:924597
Localized Corrosion of Alloy 22 -Fabrication Effects-FY05 Summary Report
Technical Report
·
Thu Oct 06 00:00:00 EDT 2005
·
OSTI ID:924597