In-Situ Observations of Sigma Phase Dissolution in 2205 Duplex Stainless Steel using Synchrotron X-Ray Diffraction
Journal Article
·
· Materials Science and Engineering A, n/a, n/a, November 30, 1999, n/a
OSTI ID:898502
Synchrotron radiation was used to directly observe the transformation of ferrite, austenite and sigma phases during heating and cooling of 2205 duplex stainless steel. Sigma formed during the initial stages of heating, dissolved as the temperature was increased, and reformed on cooling. The dissolution temperature of sigma was measured to be 985 C {+-} 2.8 C at a heating rate of 0.25 C/s, and the kinetics of sigma formation at 850 C was determined to be slower after dissolving at 1000 C than before.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 898502
- Report Number(s):
- UCRL-JRNL-223652; TRN: US0701669
- Journal Information:
- Materials Science and Engineering A, n/a, n/a, November 30, 1999, n/a, Journal Name: Materials Science and Engineering A, n/a, n/a, November 30, 1999, n/a
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-Situ Observations of Sigma Phase Dissolution in 2205 Duplex Stainless Steel Using Synchrotron X-Ray Diffraction
Direct Observations of Sigma Phase Growth and Dissolution in 2205 Duplex Stainless Steel
Direct observations of sigma phase growth and dissolution in 2205 duplex stainless steel
Journal Article
·
Mon Jan 01 00:00:00 EST 2007
· Materials Science and Engineering A
·
OSTI ID:898502
Direct Observations of Sigma Phase Growth and Dissolution in 2205 Duplex Stainless Steel
Conference
·
Tue Jun 14 00:00:00 EDT 2005
·
OSTI ID:898502
+1 more
Direct observations of sigma phase growth and dissolution in 2205 duplex stainless steel
Conference
·
Wed Oct 10 00:00:00 EDT 2007
·
OSTI ID:898502
+1 more