Evidence of Transformation Bursts During Thermal Cycling of a Pu-Ga Alloy
The thermodynamics and kinetics of the fcc (delta) to monoclinic (alpha-prime) phase transformation and its reversion in a plutonium-gallium alloy have been studied using differential scanning calorimetry, resistometry, and dilatometry. Under ambient conditions, the delta phase is metastable in a Pu-2.0 at% Ga alloy. Thermal cycling to below the ambient temperature results in a partial transformation to the alpha-prime phase; this transformation is composition-invariant and exhibits martensitic behavior. Because this transformation results in an unusually invariant large 25% volume contraction that cannot be fully accommodated by purely elastic adjustments, the transformation mode is expected to involve burst formation of individual alpha-prime particles. However, upon cooling, these individual bursts were not resolved by the above techniques, although signals corresponding to the overall accumulation of many alpha-prime particles were observed. On the other hand, upon heating, signals from differential scanning calorimetry, resistometry, and dilatometry showed a series of discrete changes occurring in periodic increments beginning at approximately 32 C. These features correspond to the cooperative reversion of many alpha-prime particles to the delta phase; they appear to be the result of an interplay between the autocatalytically driven reversion of a cascade of individual martensite units, and self-quenching caused by small changes of temperature and/or stress accompanying each individual transformation burst. The heat of the delta/alpha-prime transformation is estimated to be about + 4 kJ/mole.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 883811
- Report Number(s):
- UCRL-JRNL-209611; TRN: US200615%%262
- Journal Information:
- Metallurgical and Materials Transactions A, Vol. 37A
- Country of Publication:
- United States
- Language:
- English
Similar Records
Delta/Alpha-Prime Phase Transformations in a Pu-Ga Alloy
"Burst-like" Characteristics of the delta/alpha-prime Phase Transformation in Pu-Ga Alloys