Synthesis of Bi.sub.1.8 Pb.sub.0.4 Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.x superconductor
Patent
·
OSTI ID:870665
- Los Alamos, NM
Two-powder processes for the synthesis of superconducting (Bi, Pb)-2223/Ag-clad wires by the oxide-powder-in-the-robe are provided. The first precursor powder, of nominal stoichiometry CaCuO.sub.x, is a solution-synthesized mixture of Ca.sub.0.45 Cu.sub.0.55 O.sub.2 and CaO. Using these oxide precursor mixtures, superconducting tapes with well-aligned grains and reproducible critical current densities J.sub.c in the range of 20,000 to 26,000 A/cm.sup.2 at 75 K in self-field after annealing less than 200 hours were obtained.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- DOE Contract Number:
- W-7405-ENG-36
- Assignee:
- University of California (); Los Alamos National Laboratory ()
- Patent Number(s):
- US 5569641
- OSTI ID:
- 870665
- Country of Publication:
- United States
- Language:
- English
Synthesis of Ag-clad (Bi,Pb)-2223 tapes by an alternative precursor route
|
journal | October 1994 |
Similar Records
(Bi, Pb).sub.2, Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.x superconductor and method of making same utilizing sinter-forging
Synthesis of Bi{sub 1.8}Pb{sub 0.4}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub x} superconductor
Synthesis of BiPbSrCaCuO superconductor
Patent
·
Thu Jan 01 00:00:00 EST 1998
·
OSTI ID:870665
Synthesis of Bi{sub 1.8}Pb{sub 0.4}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub x} superconductor
Patent
·
Tue Oct 29 00:00:00 EST 1996
·
OSTI ID:870665
Synthesis of BiPbSrCaCuO superconductor
Patent
·
Sat Jan 01 00:00:00 EST 1994
·
OSTI ID:870665
+2 more
Related Subjects
synthesis
pb
sr
cu
superconductor
two-powder
processes
superconducting
-2223
ag-clad
wires
oxide-powder-in-the-robe
provided
precursor
powder
nominal
stoichiometry
cacuo
solution-synthesized
mixture
45
55
cao
oxide
mixtures
tapes
well-aligned
grains
reproducible
critical
current
densities
range
20
000
26
cm
75
self-field
annealing
200
hours
obtained
precursor mixture
current densities
critical current
precursor powder
precursor mixtures
oxide precursor
superconducting tape
/505/252/423/
pb
sr
cu
superconductor
two-powder
processes
superconducting
-2223
ag-clad
wires
oxide-powder-in-the-robe
provided
precursor
powder
nominal
stoichiometry
cacuo
solution-synthesized
mixture
45
55
cao
oxide
mixtures
tapes
well-aligned
grains
reproducible
critical
current
densities
range
20
000
26
cm
75
self-field
annealing
200
hours
obtained
precursor mixture
current densities
critical current
precursor powder
precursor mixtures
oxide precursor
superconducting tape
/505/252/423/