Process for fabrication of large titanium diboride ceramic bodies
Patent
·
OSTI ID:866873
- Knoxville, TN
A process for manufacturing large, fully dense, high purity TiB.sub.2 articles by pressing powders with a sintering aid at relatively low temperatures to reduce grain growth. The process requires stringent temperature and pressure applications in the hot-pressing step to ensure maximum removal of sintering aid and to avoid damage to the fabricated article or the die.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC05-84OR21400
- Assignee:
- United States of America as represented by Department of Energy (Washington, DC)
- Patent Number(s):
- US 4812280
- OSTI ID:
- 866873
- Country of Publication:
- United States
- Language:
- English
Similar Records
Process for fabrication of large titanium diboride ceramic bodies
Process for fabrication of large titanium diboride ceramic bodies
Fabrication of large-volume, low-cost ceramic lanthanum halide scintillators for gamma ray detection : final report for DHS/DNDO/TRDD project TA-01-SL01.
Patent
·
Thu Apr 17 00:00:00 EST 1986
·
OSTI ID:866873
Process for fabrication of large titanium diboride ceramic bodies
Patent
·
Tue Mar 14 00:00:00 EST 1989
·
OSTI ID:866873
Fabrication of large-volume, low-cost ceramic lanthanum halide scintillators for gamma ray detection : final report for DHS/DNDO/TRDD project TA-01-SL01.
Technical Report
·
Wed Oct 01 00:00:00 EDT 2008
·
OSTI ID:866873
+3 more
Related Subjects
process
fabrication
titanium
diboride
ceramic
bodies
manufacturing
dense
purity
tib
articles
pressing
powders
sintering
relatively
temperatures
reduce
grain
growth
requires
stringent
temperature
pressure
applications
hot-pressing
step
ensure
maximum
removal
avoid
damage
fabricated
article
die
avoid damage
titanium diboride
ceramic bodies
grain growth
diboride ceramic
/264/501/
fabrication
titanium
diboride
ceramic
bodies
manufacturing
dense
purity
tib
articles
pressing
powders
sintering
relatively
temperatures
reduce
grain
growth
requires
stringent
temperature
pressure
applications
hot-pressing
step
ensure
maximum
removal
avoid
damage
fabricated
article
die
avoid damage
titanium diboride
ceramic bodies
grain growth
diboride ceramic
/264/501/