Quick setting water-compatible furfuryl alcohol polymer concretes
Patent
·
OSTI ID:864423
- Ridge, NY
- Port Jefferson, NY
- Brookhaven, NY
A novel quick setting polymer concrete composite comprising a furfuryl alcohol monomer, an aggregate containing a maximum of 8% by weight water, and about 1-10% trichlorotoluene initiator and about 20-80% powdered metal salt promoter, such as zinc chloride, based on the weight of said monomer, to initiate and promote polymerization of said monomer in the presence of said aggregate, within 1 hour after mixing at a temperature of -20.degree. C. to 40.degree. C., to produce a polymer concrete having a 1 hour compressive strength greater than 2000 psi.
- Research Organization:
- Associated Universities, Inc., Upton, NY (United States)
- DOE Contract Number:
- AC02-76CH00016
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4361670
- Application Number:
- 06/260,623
- OSTI ID:
- 864423
- Country of Publication:
- United States
- Language:
- English
Similar Records
Quick setting water-compatible furfuryl alcohol polymer concretes
Furfuryl alcohol polymer concretes for use in all-weather repairs of concrete and asphalt surfaces. Revision
Furfuryl alcohol polymer concretes for use in all-weather repairs of concrete and asphalt surfaces
Patent
·
Tue Nov 30 00:00:00 EST 1982
·
OSTI ID:864423
Furfuryl alcohol polymer concretes for use in all-weather repairs of concrete and asphalt surfaces. Revision
Conference
·
Mon Apr 01 00:00:00 EST 1985
·
OSTI ID:864423
Furfuryl alcohol polymer concretes for use in all-weather repairs of concrete and asphalt surfaces
Conference
·
Mon Apr 01 00:00:00 EST 1985
·
OSTI ID:864423
Related Subjects
quick
setting
water-compatible
furfuryl
alcohol
polymer
concretes
novel
concrete
composite
comprising
monomer
aggregate
containing
maximum
weight
water
1-10
trichlorotoluene
initiator
20-80
powdered
metal
salt
promoter
zinc
chloride
based
initiate
promote
polymerization
presence
hour
mixing
temperature
-20
degree
40
produce
compressive
strength
2000
psi
quick setting
compressive strength
metal salt
zinc chloride
composite comprising
powdered metal
polymer concrete
weight water
furfuryl alcohol
setting polymer
/524/525/
setting
water-compatible
furfuryl
alcohol
polymer
concretes
novel
concrete
composite
comprising
monomer
aggregate
containing
maximum
weight
water
1-10
trichlorotoluene
initiator
20-80
powdered
metal
salt
promoter
zinc
chloride
based
initiate
promote
polymerization
presence
hour
mixing
temperature
-20
degree
40
produce
compressive
strength
2000
psi
quick setting
compressive strength
metal salt
zinc chloride
composite comprising
powdered metal
polymer concrete
weight water
furfuryl alcohol
setting polymer
/524/525/