Process for diffusing metallic coatings into ceramics to improve their voltage withstanding capabilities
Patent
·
OSTI ID:862995
- Clearwater, FL
- St. Petersburg, FL
The disclosure relates to a method for diffusing a coating of manganese powder and titanium powder into a ceramic to improve its voltage hold off withstanding capability. The powder coated ceramic is fired for from about 30 to about 90 minutes within about one atmosphere of wet hydrogen at a temperature within the range of from about 1450.degree. to about 1520.degree. C to cause the mixture to penetrate into the ceramic to a depth on the order of a millimeter.
- Research Organization:
- General Electric Co., Boston, MA (United States)
- DOE Contract Number:
- AT(29-2)-656
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4069357
- OSTI ID:
- 862995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Process for diffusing metallic coatings into ceramics to improve their voltage withstanding capabilities
Process for diffusing metallic coatings into ceramics to improve their voltage withstanding
Metal matrix composite of an iron aluminide and ceramic particles and method thereof
Patent
·
Tue Jan 17 00:00:00 EST 1978
·
OSTI ID:862995
Process for diffusing metallic coatings into ceramics to improve their voltage withstanding
Patent
·
Tue Nov 09 00:00:00 EST 1976
·
OSTI ID:862995
Metal matrix composite of an iron aluminide and ceramic particles and method thereof
Patent
·
Wed Jan 01 00:00:00 EST 1997
·
OSTI ID:862995
Related Subjects
process
diffusing
metallic
coatings
ceramics
improve
voltage
withstanding
capabilities
disclosure
relates
method
coating
manganese
powder
titanium
ceramic
hold
capability
coated
fired
30
90
minutes
atmosphere
wet
hydrogen
temperature
range
1450
degree
1520
mixture
penetrate
depth
millimeter
metallic coating
disclosure relates
coated ceramic
metallic coatings
titanium powder
wet hydrogen
voltage hold
/427/174/428/
diffusing
metallic
coatings
ceramics
improve
voltage
withstanding
capabilities
disclosure
relates
method
coating
manganese
powder
titanium
ceramic
hold
capability
coated
fired
30
90
minutes
atmosphere
wet
hydrogen
temperature
range
1450
degree
1520
mixture
penetrate
depth
millimeter
metallic coating
disclosure relates
coated ceramic
metallic coatings
titanium powder
wet hydrogen
voltage hold
/427/174/428/