Effects of titanium additions to austenitic ternary alloys on microstructural evolution and void swelling
Journal Article
·
· Philosophical Magazine
OSTI ID:862207
Ternary austenitic model alloys were modified with 0.25 wt.% titanium and irradiated in FFTF reactor at dose rates ranging over more than two orders in magnitude. While lowering of dose rate strongly increases swelling by shortening the incubation dose, the steady state swelling rate is not affected by dose rate. Although titanium addition strongly alters the void microstructure, swelling at {approx} 420 C does not change with titanium additions, but the sensitivity to dose rate is preserved.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 862207
- Report Number(s):
- UCRL-JRNL-201230; TRN: US200602%%366
- Journal Information:
- Philosophical Magazine, Vol. 85, Issue 18
- Country of Publication:
- United States
- Language:
- English
Similar Records
Boron Addition to Model Austenitic Steels and void Nucleation
Neutron-Induced Microstructural Evolution of Fe-15Cr-16Ni Alloys at ~400 C During Neutron Irradiation in the FFTF Fast Reactor
Assessment of void swelling in austenitic stainless steel PWR core internals.
Conference
·
Thu Oct 30 00:00:00 EST 2003
·
OSTI ID:862207
+1 more
Neutron-Induced Microstructural Evolution of Fe-15Cr-16Ni Alloys at ~400 C During Neutron Irradiation in the FFTF Fast Reactor
Book
·
Sat Jun 30 00:00:00 EDT 2001
·
OSTI ID:862207
+4 more
Assessment of void swelling in austenitic stainless steel PWR core internals.
Technical Report
·
Tue Jan 31 00:00:00 EST 2006
·
OSTI ID:862207