Hydrogen Induced Cracking of Drip Shield
One potential failure mechanism for titanium and its alloys under repository conditions is via the absorption of atomic hydrogen in the metal crystal lattice. The resulting decreased ductility and fracture toughness may lead to brittle mechanical fracture called hydrogen-induced cracking (HIC) or hydrogen embrittlement. For the current design of the engineered barrier without backfill, HIC may be a problem since the titanium drip shield can be galvanically coupled to rock bolts (or wire mesh), which may fall onto the drip shield, thereby creating conditions for hydrogen production by electrochemical reaction. The purpose of this scientific analysis and modeling activity is to evaluate whether the drip shield will fail by HIC or not under repository conditions within 10,000 years of emplacement. This Analysis and Model Report (AMR) addresses features, events, and processes related to hydrogen induced cracking of the drip shield. REV 00 of this AMR served as a feed to ''Waste Package Degradation Process Model Report'' and was developed in accordance with the activity section ''Hydrogen Induced Cracking of Drip Shield'' of the development plan entitled ''Analysis and Model Reports to Support Waste Package PMR'' (CRWMS M&O 1999a). This AMR, prepared according to ''Technical Work Plan for: Waste Package Materials Data Analyses and Modeling'' (BSC 2002), is to feed the License Application.
- Research Organization:
- Yucca Mountain Project, Las Vegas, NV (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- OSTI ID:
- 836507
- Report Number(s):
- ANL-EBS-MD-000006, Rev. 01; DOC.20030304.0003, DC No. 32434; TRN: US200504%%98
- Resource Relation:
- Other Information: PBD: 24 Feb 2003
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen-Induced Cracking of the Drip Shield
General Corrosion and Localized Corrosion of the Drip Shield