Relationships between processing temperature and microstructure in isothermal melt processed Bi-2212 thick films
Conference
·
OSTI ID:81118
The microstructure and phase assemblage of isothermal melt processed (IMP) Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub y} (Bi-2212) thick films have been evaluated. Results from compositional analysis and phase identification indicate that the characteristics of the partial melt greatly influence the microstructural and chemical development of the thick films. The highest critical current densities were obtained in films processed below 800{degrees}C where the partial melt uniformly coats the substrate without excessive phase segregation.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 81118
- Report Number(s):
- LA-UR-95-1324; CONF-941013-38; ON: DE95012070
- Resource Relation:
- Conference: Applied superconductivity conference, Boston, MA (United States), 16-21 Oct 1994; Other Information: PBD: [1995]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Al{sub 2}O{sub 3} additions for isothermal melt processing of Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub {ital y}}
Processing and properties of Bi-2212 thick films
Tape casting and partial melting of Bi-2212 thick films
Journal Article
·
Sun Sep 01 00:00:00 EDT 1996
· Journal of Materials Research
·
OSTI ID:81118
Processing and properties of Bi-2212 thick films
Book
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:81118
+1 more
Tape casting and partial melting of Bi-2212 thick films
Conference
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:81118