Hydrogen Storage Properties of Lithium Aluminohydride Modified by Dopants and Mechanochemistry
- Iowa State Univ., Ames, IA (United States)
Alkali metal aluminohydrides have high potential as solid hydrogen storage materials. They have been known for their irreversible dehydrogenation process below 100 atm until Bogdanovic et al [1, 2] succeeded in the re-hydrogenation of NaAlH4 below 70 atm. They achieved 4 wt.% H2 reversible capacity by doping NaAlH4 with Ti and/or Fe organo-metalic compounds as catalysts. This suggests that other alkali and, possibly alkaline earth metal aluminohydrides can be used for reversible hydrogen storage when modified by proper dopants. In this research, Zr27Ti9Ni38V5Mn16Cr5, LaNi4.85Sn0.15, Al3Ti, and PdCl2 were combined , LaNi4.85Sn0.15, Al3Ti, and PdCl2 were combined with LiAlH4 by ball-milling to study whether or not LiAlH4 is capable to both absorb and desorb hydrogen near ambient conditions. X-ray powder diffraction, differential thermal analysis, and scanning electron microscopy were employed for sample characterizations. All four compounds worked as catalysts in the dehydrogenation reactions of both LiAlH4 and Li3AlH6 by inducing the decomposition at lower temperature. However, none of them was applicable as catalyst in the reverse hydrogenation reaction at low to moderate hydrogen pressure.
- Research Organization:
- Ames Lab., Ames, IA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- W-7405-Eng-82
- OSTI ID:
- 798523
- Report Number(s):
- IS-T 2068; TRN: US200216%%216
- Resource Relation:
- Other Information: TH: Thesis (M.S.); Submitted to Iowa State Univ., Ames, IA (US); PBD: 1 Aug 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen Storage Properties of Lithium Aluminohydride Modified by Dopants and Mechanochemistry
Final Report: DE- FC36-05GO15063, Fundamental Studies of Advanced High-Capacity, Reversible Metal Hydrides