Fundamental metallurgical aspects of axial splitting in zircaloy cladding
Fundamental metallurgical aspects of axial splitting in irradiated Zircaloy cladding have been investigated by microstructural characterization and analytical modeling, with emphasis on application of the results to understand high-burnup fuel failure under RIA situations. Optical microscopy, SEM, and TEM were conducted on BWR and PWR fuel cladding tubes that were irradiated to fluence levels of 3.3 x 10{sup 21} n cm{sup {minus}2} to 5.9 x 10{sup 21} n cm{sup {minus}2} (E > 1 MeV) and tested in hot cell at 292--325 C in Ar. The morphology, distribution, and habit planes of macroscopic and microscopic hydrides in as-irradiated and posttest cladding were determined by stereo-TEM. The type and magnitude of the residual stress produced in association with oxide-layer growth and dense hydride precipitation, and several synergistic factors that strongly influence axial-splitting behavior were analyzed. The results of the microstructural characterization and stress analyses were then correlated with axial-splitting behavior of high-burnup PWR cladding reported for simulated-RIA conditions. The effects of key test procedures and their implications for the interpretation of RIA test results are discussed.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 754479
- Report Number(s):
- ANL/ET/CP-101429; TRN: US0002771
- Resource Relation:
- Conference: International Topical Meeting on Light Water Reactor Fuel Performance, Park City, UT (US), 04/10/2000--04/13/2000; Other Information: PBD: 3 Apr 2000
- Country of Publication:
- United States
- Language:
- English
Similar Records
The PROMETRA program: plane strain tests on fresh and highly irradiated zircaloy-4, ZIRLO and M5 fuel claddings
Effect of irradiation on the microstructure of Zircaloy-4