Aluminum oxide film thickness and emittance
Aluminum reactor components which are not actively cooled could be subjected to high temperatures due to gamma heating after the core coolant level dropped during the ECS phase of a hypothetical LOCA event. Radiative heat transfer is the dominant heat transfer process in this scenario and therefore the emittance of these components is of interest. Of particular interest are the safety rod thimbles and Mark 60B blanket assemblies; for the K Reactor, these components have been exposed to low temperature (< 55{degrees}C) moderator for about a year. The average moderator temperature was assumed to be 30{degrees}C. The Al oxide film thickness at this temperature, after one year of exposure, is predicted to be 6.4 {mu}m {plus minus} 10%; insensitive to exposure time. Dehydration of the film during the gamma heating accident would result in a film thickness of 6.0 {mu}m {plus minus} 11%. Total hemispherical emittance is predicted to be 0.69 at 96{degrees}C, decreasing to 0.45 at 600{degrees}C. Some phenomena which would tend to yield thicker oxide films in the reactor environment relative to those obtained under experimental conditions were neglected and the predicted film thickness values are therefore conservative. The emittance values predicted for a given film thickness are also conservative. The conservativisms inherent in the predicted emittance are particularly relevant for uncertainty analysis of temperatures generated using these values.
- Research Organization:
- Savannah River Site (SRS), Aiken, SC (United States)
- Sponsoring Organization:
- USDOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC09-89SR18035; AC09-76SR00001
- OSTI ID:
- 7102414
- Report Number(s):
- WSRC-RD-91-24; ON: DE92019931
- Country of Publication:
- United States
- Language:
- English
Similar Records
EBR-II FUEL IRRADIATION FACILITIES
Annual Report: Fuels (30 September 2012)
Related Subjects
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS
36 MATERIALS SCIENCE
ALUMINIUM
CORROSION
ALUMINIUM OXIDES
EMISSIVITY
PRODUCTION REACTORS
LOSS OF COOLANT
REACTOR COMPONENTS
RADIATION HEATING
DEHYDRATION
FILMS
GAMMA RADIATION
K REACTOR
OXIDATION
THICKNESS
WATER
ACCIDENTS
ALUMINIUM COMPOUNDS
CHALCOGENIDES
CHEMICAL REACTIONS
DIMENSIONS
ELECTROMAGNETIC RADIATION
ELEMENTS
HEATING
HEAVY WATER MODERATED REACTORS
HYDROGEN COMPOUNDS
IONIZING RADIATIONS
METALS
OPTICAL PROPERTIES
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
RADIATIONS
REACTOR ACCIDENTS
REACTORS
SPECIAL PRODUCTION REACTORS
SURFACE PROPERTIES
220900* - Nuclear Reactor Technology- Reactor Safety
220600 - Nuclear Reactor Technology- Research
Test & Experimental Reactors
360204 - Ceramics
Cermets
& Refractories- Physical Properties
360205 - Ceramics
Cermets
& Refractories- Corrosion & Erosion