Micelle-derived catalysts for extended Schulz-Flory
The reduced C-73-1-101 iron catalyst was retested in Run 10, under the third set of reference conditions: 208[degree]C, 500 psig, 0.9 (molar) H[sub 2]/CO feed ratio, [approximately] 35% initial CO conversion. The analysis of the products collected during the entire 252-hour run, including the wax recovered from the catalyst, resulted in [alpha] = 0.78 for carbon numbers 1 to 15 and [alpha] = 0.88 for carbon numbers 16 to 45. The results of Run 10 are satisfactory and will be used in the future as reference performance. No further tests with the reference catalyst are going to be conducted until a method for testing experimental catalysts is established and new reference performance under different conditions is necessitated. Ruthenium particles, mostly in the 40 to 60 [Angstrom] size range, were prepared on the [gamma]-alumina by using a micelle technique. The narrow size distribution of ruthenium particles was not maintained and some very large particles up to 1000 [Angstrom] resulted when the catalyst preparation was upscaled from 2 g to [approximately] 30 g. The causes of the maldistribution that occurred during the scaling up of the catalyst preparation are under investigation. The catalyst which showed broad size distribution of ruthenium particles showed rapid deactivation during a test in Plant 700. Investigations are under way to improve the catalytic stability. Small angle X-ray scattering was used to characterize the reversed micelle solution used in the preparation of ruthenium catalysts. The volume averaged diameter of the water core for the reversed micelles is between 75 and 90 [Angstrom].
- Research Organization:
- UOP, Inc., Des Plaines, IL (United States). Signal UOP Research Center
- Sponsoring Organization:
- USDOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC22-84PC70023
- OSTI ID:
- 6995128
- Report Number(s):
- DOE/PC/70023-T3; ON: DE93003291
- Country of Publication:
- United States
- Language:
- English
Similar Records
Micelle-derived catalysts for extended Schulz-Flory. [Quarterly report], January 1, 1986--March 31, 1986
Micelle-derived catalysts for extended Schulz-Flory
Related Subjects
CATALYSTS
CHEMICAL PREPARATION
PERFORMANCE TESTING
FISCHER-TROPSCH SYNTHESIS
IRON
CATALYTIC EFFECTS
RUTHENIUM
SYNTHESIS GAS
CONVERSION
ALUMINIUM OXIDES
CATALYST SUPPORTS
EXPERIMENTAL DATA
PROGRESS REPORT
SMALL ANGLE SCATTERING
ALUMINIUM COMPOUNDS
CHALCOGENIDES
CHEMICAL REACTIONS
DATA
DOCUMENT TYPES
ELEMENTS
FLUIDS
GASES
INFORMATION
METALS
NUMERICAL DATA
OXIDES
OXYGEN COMPOUNDS
PLATINUM METALS
SCATTERING
SYNTHESIS
TESTING
TRANSITION ELEMENTS
010408* - Coal
Lignite
& Peat- C1 Processes- (1987-)