Embrittlement of Cr-Mo steels in H/sub 2/S plus H/sub 2/O vapor environment. Quarterly report No. 8, May 15-August 15, 1980
In previous tests the environment was H/sub 2/S of the highest commercially available purity. In this environment it proved impossible, by our current techniques, to induce hydrogen embrittlement in low yield strength (45 to 75 ksi or 300 to 500 MPa) samples which had been given a post weld heat treatment. The introduction of saturated water vapor in the H/sub 2/S has clearly served to give conditions in which the lower strength steels can be embrittled.
- Research Organization:
- Westinghouse Research and Development Center, Pittsburgh, PA (USA)
- DOE Contract Number:
- AC05-78ET13513
- OSTI ID:
- 6877452
- Report Number(s):
- DOE/ET/13513-T7
- Country of Publication:
- United States
- Language:
- English
Similar Records
Contract WEC 3. 2. 3 study to optimize Cr-Mo steels to resist hydrogen and temper embrittlement. Quarterly report No. 8, May 15-August 15, 1980. Embrittlement of Cr-Mo steels in H/sub 2/S plus H/sub 2/O vapor environment
Embrittlement of Cr-Mo steels in H/sub 2/S plus H/sub 2/O vapor environment. Quarterly report No. 8, May 15-August 15, 1980
Contract WEC 3. 2. 3 study to optimize Cr-Mo steels to resist hydrogen and temper embrittlement. Quarterly report No. 9, second annual report, January 1-December 31, 1980
Technical Report
·
Fri Nov 28 00:00:00 EST 1980
·
OSTI ID:6877452
Embrittlement of Cr-Mo steels in H/sub 2/S plus H/sub 2/O vapor environment. Quarterly report No. 8, May 15-August 15, 1980
Technical Report
·
Fri Nov 28 00:00:00 EST 1980
·
OSTI ID:6877452
Contract WEC 3. 2. 3 study to optimize Cr-Mo steels to resist hydrogen and temper embrittlement. Quarterly report No. 9, second annual report, January 1-December 31, 1980
Technical Report
·
Tue Jan 20 00:00:00 EST 1981
·
OSTI ID:6877452
Related Subjects
36 MATERIALS SCIENCE
CHROMIUM-MOLYBDENUM STEELS
FRACTURE PROPERTIES
HYDROGEN EMBRITTLEMENT
HYDROGEN
METALLURGICAL EFFECTS
CHARPY TEST
CRACKS
EXPERIMENTAL DATA
GROWTH
HEAT TREATMENTS
HYDROGEN SULFIDES
METALLOGRAPHY
WELDED JOINTS
ALLOYS
CHALCOGENIDES
CHROMIUM ALLOYS
CHROMIUM STEELS
DATA
DESTRUCTIVE TESTING
ELEMENTS
EMBRITTLEMENT
HYDROGEN COMPOUNDS
IMPACT TESTS
INFORMATION
IRON ALLOYS
IRON BASE ALLOYS
JOINTS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICAL TESTS
NONMETALS
NUMERICAL DATA
STEELS
SULFIDES
SULFUR COMPOUNDS
TESTING
360105* - Metals & Alloys- Corrosion & Erosion
CHROMIUM-MOLYBDENUM STEELS
FRACTURE PROPERTIES
HYDROGEN EMBRITTLEMENT
HYDROGEN
METALLURGICAL EFFECTS
CHARPY TEST
CRACKS
EXPERIMENTAL DATA
GROWTH
HEAT TREATMENTS
HYDROGEN SULFIDES
METALLOGRAPHY
WELDED JOINTS
ALLOYS
CHALCOGENIDES
CHROMIUM ALLOYS
CHROMIUM STEELS
DATA
DESTRUCTIVE TESTING
ELEMENTS
EMBRITTLEMENT
HYDROGEN COMPOUNDS
IMPACT TESTS
INFORMATION
IRON ALLOYS
IRON BASE ALLOYS
JOINTS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICAL TESTS
NONMETALS
NUMERICAL DATA
STEELS
SULFIDES
SULFUR COMPOUNDS
TESTING
360105* - Metals & Alloys- Corrosion & Erosion