Dialkylenecarbonate-Bridged Polysilsesquioxanes. Hybrid Organic Sol-Gels with a Thermally Labile Bridging Group
In this paper, we introduce a new approach for altering the properties of bridged polysilsesquioxane xerogels using post-processing modification of the polymeric network. The bridging organic group contains latent functionalities that can be liberated thermally, photochemically, or by chemical means after the gel has been processed to a xerogel. These modifications can produce changes in density, volubility, porosity, and or chemical properties of the material. Since every monomer possesses two latent functional groups, the technique allows for the introduction of high levels of functionality in hybrid organic-inorganic materials. Dialkylenecarbonate-bridged polysilsesquioxane gels were prepared by the sol-gel polymerization of bis(triethoxysilylpropyl)carbonate (1) and bis(triethoxysilylisobutyl)-carbonate (2). Thermal treatment of the resulting non-porous xerogels and aerogels at 300-350 C resulted in quantitative decarboxylation of the dialkylenecarbonate bridging groups to give new hydroxyalkyl and olefinic substituted polysilsesquioxane monolithic xerogels and aerogels that can not be directly prepared through direct sol-gel polymerization of organotrialkoxysilanes.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sandia National Lab. (SNL-CA), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- OSTI ID:
- 5905
- Report Number(s):
- SAND99-0995J; TRN: AH200115%%133
- Journal Information:
- Journal of the American Chemical Society, Other Information: Submitted to Journal of the American Chemical Society; PBD: 21 Apr 1999
- Country of Publication:
- United States
- Language:
- English