Soldering of Thin Film-Metallized Glass Substrates
The ability to produce reliable electrical and structural interconnections between glass and metals by soldering was investigated. Soldering generally requires premetallization of the glass. As a solderable surface finish over soda-lime-silicate glass, two thin films coatings, Cr-Pd-Au and NiCr-Sn, were evaluated. Solder nettability and joint strengths were determined. Test samples were processed with Sn60-Pb40 solder alloy at a reflow temperature of 210 C. Glass-to-cold rolled steel single lap samples yielded an average shear strength of 12 MPa. Solder fill was good. Control of the Au thickness was critical in minimizing the formation of AuSn{sub 4} intermetallic in the joint, with a resulting joint shear strength of 15 MPa. Similar glass-to-glass specimens with the Cr-Pd-Au finish failed at 16.5 MPa. The NiCr-Sn thin film gave even higher shear strengths of 20-22.5 MPa, with failures primarily in the glass.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sandia National Lab. (SNL-CA), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 5675
- Report Number(s):
- SAND98-2081; TRN: AH200115%%168
- Resource Relation:
- Conference: InterPACK'99, Lahaina, HI (US), 06/13/1999--06/19/1999; Other Information: PBD: 31 Mar 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Gold-Tin Solder Wetting Behavior for Package Lid Seals
Growth of a Au-Ni-Sn intermetallic compound on the solder-substrate interface after aging