Effect of test temperature and strain rate on the tensile properties of high-strength, high-conductivity copper alloys
- Oak Ridge National Lab., TN (United States)
The unirradiated tensile properties of wrought GlidCop AL25 (ITER grade zero, IGO) solutionized and aged CuCrZr, and cold-worked and aged and solutionized and aged Hycon 3HP{trademark} CuNiBe have been measured over the temperature range of 20-500{degrees}C at strain rates between 4 x 10{sup {minus}4} s{sup {minus}1} and 0.06 s{sup {minus}1}. The measured room temperature electrical conductivity ranged from 64 to 90% IACS for the different alloys. All of the alloys were relatively insensitive to strain rate at room temperature, but the strain rate sensitivity of GlidCop Al25 increased significantly with increasing temperature. The CuNiBe alloys exhibited the best combination of high strength and high conductivity at room temperature. The strength of CuNiBe decreased slowly with increasing temperature. However, the ductility of CuNiBe decreased rapidly with increasing temperature due to localized deformation near grain boundaries, making these alloy heats unsuitable for typical structural applications above 300{degrees}C. The strength and uniform elongation of GlidCop Al25 decreased significantly with increasing temperature at a strain rate of 1 x 10{sup {minus}3} s{sup {minus}1}, whereas the total elongation was independent of test temperature. The strength and ductility of CuCrZr decreased slowly with increasing temperature.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- OSTI ID:
- 543291
- Report Number(s):
- DOE/ER-0313/21; ON: DE97008798; TRN: 97:020333
- Resource Relation:
- Other Information: PBD: Apr 1997; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1996; PB: 296 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of heat treatments on the tensile and electrical properties of high-strength, high-conductivity copper alloys
Evaluation of high strength, high conductivity CuNiBe alloys for fusion energy applications