Synthesis, characterization and mechanical properties of nanocrystalline NiAl
Conference
·
OSTI ID:446025
- Illinois Inst. of Tech., Chicago, IL (United States). Dept. of Mechanical, Materials and Aerospace Engineering
- Argonne National Lab., IL (United States)
Nanocrystalline NiAl was produced from pre-cast alloys using an electron beam inert gas condensation system. In-situ compaction was carried out at 100-300 C under vacuum conditions. Energy dispersive spectroscopy was used to determine chemical composition and homogeneity. Average grain sizes in the range 4-10 nm were found from TEM dark field analyses. A compression-cage fixture was designed to perform disk bend tests. These tests revealed substantial room temperature ductility in nanocrystalline NiAl, while coarse grained NiAl showed no measurable room temperature ductility.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Energy Research, Washington, DC (United States); Department of Defense, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 446025
- Report Number(s):
- ANL/MSD/CP-91826; CONF-961202-32; ON: DE97001967; CNN: Grant FY9620-92-J
- Resource Relation:
- Conference: 1996 Fall meeting of the Materials Research Society (MRS), Boston, MA (United States), 2-6 Dec 1996; Other Information: PBD: Nov 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanical properties of nanocrystalline metals, intermetalics and multiphase materials determined by tension, compression and disk-bend techniques
Nanocrystalline NiA1 - processing, characterization and mechanical properties.
Evidence of room temperature ductility in nanocrystalline NiAl from biaxial disk bend tests
Conference
·
Sat Feb 01 00:00:00 EST 1997
·
OSTI ID:446025
+3 more
Nanocrystalline NiA1 - processing, characterization and mechanical properties.
Journal Article
·
Sun Nov 15 00:00:00 EST 1998
· Mater. Sci. Eng. A
·
OSTI ID:446025
Evidence of room temperature ductility in nanocrystalline NiAl from biaxial disk bend tests
Journal Article
·
Mon Sep 15 00:00:00 EDT 1997
· Scripta Materialia
·
OSTI ID:446025
+1 more