In-situ measurement of the electrical conductivity of aluminum oxide in HFIR
- Oak Ridge National Lab., TN (United States); and others
A collaborative DOE/Monbusho irradiation experiment has been completed which measured the in-situ electrical resistivity of 12 different grades of aluminum oxide during HFIR neutron irradiation at 450{degrees}C. No evidence for bulk RIED was observed following irradiation to a maximum dose of 3 dpa with an applied dc electric field of 200 V/mm.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- OSTI ID:
- 414885
- Report Number(s):
- DOE/ER-0313/20; ON: DE97000700; TRN: 97:001404
- Resource Relation:
- Other Information: PBD: Oct 1996; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending June 30, 1996; PB: 358 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Capsule fabrication for in-situ measurement of radiation induced electrical degradation (RIED) of ceramics in HFIR
Analysis of in-situ electrical conductivity data from the HFIR TRIST-ER1 experiment
Proceedings of the ninth IEA workshop on radiation effects in ceramic insulators
Technical Report
·
Mon Apr 01 00:00:00 EST 1996
·
OSTI ID:414885
+1 more
Analysis of in-situ electrical conductivity data from the HFIR TRIST-ER1 experiment
Technical Report
·
Fri Aug 01 00:00:00 EDT 1997
·
OSTI ID:414885
Proceedings of the ninth IEA workshop on radiation effects in ceramic insulators
Conference
·
Wed Dec 31 00:00:00 EST 1997
·
OSTI ID:414885
+1 more