Low-temperature low-dose neutron irradiation effects on Brush Wellman S65-C and Kawechi Berylco P0 beryllium
- Oak Ridge National Lab., TN (United States)
The mechanical property results for two high quality beryllium materials subjected to low temperature, low dose neutron irradiation in water moderated reactors are presented. Materials chosen were the S65-C ITER candidate material produced by Brush Wellman, and Kawecki Berylco Industries P0 beryllium. Both materials were processed by vacuum hot pressing. Mini sheet tensile and thermal diffusivity specimens were irradiated in the temperature range of {approximately}100--275 C from a fast (E > 0.1 MeV) neutron dose of 0.05 to 1.0 {times} 10{sup 25} n/m{sup 2} in the High Flux Isotope Reactor (HFIR) at the Oak Ridge National Laboratory and the High Flux Beam Reactor (HFBR) at the Brookhaven National Laboratory. As expected from earlier work on beryllium, both materials underwent significant embrittlement with corresponding reduction in ductility and increased strength. Both thermal diffusivity and volumetric expansion were measured and found to be negligible in this temperature and fluence range. Of significance from this work is that while both materials rapidly embrittle at these ITER relevant irradiation conditions, some ductility (>1--2%) remains, which contrasts with a body of earlier work including recent work on the Brush-Wellman S65-C material irradiated to slightly higher neutron fluence.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 330631
- Report Number(s):
- DOE/ER-0313/24; ON: DE98007433; TRN: 99:005086
- Resource Relation:
- Other Information: PBD: Sep 1998; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending June 30, 1998; Burn, G. [ed.] [comp.]; PB: 314 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Comparison of properties and microstructures of Trefimetaux and Hycon 3HP{trademark} after neutron irradiation
Proton irradiation effects on beryllium – A macroscopic assessment