Immersion studies on candidate container alloys for the Tuff Repository
- Cortest Columbus Technologies, OH (USA)
Cortest Columbus Technologies (CC Technologies) is investigating the long-term performance of container materials used for high-level radioactive waste packages. This information is being developed for the Nuclear Regulatory Commission to aid in their assessment of the Department of Energy`s application to construct a geologic repository for disposal of high-level radioactive waste. This report summarizes the results of exposure studies performed on two copper-base and two Fe-Cr-Ni alloys in simulated Tuff Repository conditions. Testing was performed at 90{degrees}C in three environments; simulated J-13 well water, and two environments that simulated the chemical effects resulting from boiling and irradiation of the groundwater. Creviced specimens and U-bends were exposed to liquid, to vapor above the condensed phase, and to alternate immersion. A rod specimen was used to monitor corrosion at the vapor-liquid interface. The specimens were evaluated by electrochemical, gravimetric, and metallographic techniques following approximately 2000 hours of exposure. Results of the exposure tests indicated that all four alloys exhibited acceptable general corrosion rates in simulated J-13 well water. These rates decreased with time. Incipient pitting was observed under deposits on Alloy 825 and pitting was observed on both Alloy CDA 102 and Alloy CDA 715 in the simulated J-13 well water. No SCC was observed in U-bend specimens of any of the alloys in simulated J-13 well water. 33 refs., 48 figs., 23 tabs.
- Research Organization:
- US Nuclear Regulatory Commission (NRC), Washington, DC (United States). Div. of Engineering; Cortest Columbus Technologies, Inc., OH (United States)
- Sponsoring Organization:
- Nuclear Regulatory Commission, Washington, DC (USA)
- OSTI ID:
- 138113
- Report Number(s):
- NUREG/CR-5598; ON: TI91012462; TRN: 91:019283
- Resource Relation:
- Other Information: PBD: May 1991
- Country of Publication:
- United States
- Language:
- English
Similar Records
Pitting, galvanic, and long-term corrosion studies on candidate container alloys for the Tuff Repository
Pitting, galvanic, and long-term corrosion studies on candidate container alloys for the Tuff Repository