W and WSi(x) Ohmic Contacts on p- And n-Type GaN
W and WSi ohmic contacts on both p- and n-type GaN have been annealed at temperatures from 300-1000 *C. There is minimal reaction (< 100 ~ broadening of the metal/GaN interface) even at 1000 *C. Specific contact resistances in the 10-5 f2-cm2 range are obtained for WSiX on Si-implanted GaN with a peak doping concentration of- 5 x 1020 cm-3, after annealing at 950 `C. On p-GaN, leaky Schottky diode behavior is observed for W, WSiX and Ni/Au contacts at room temperature, but true ohmic characteristics are obtained at 250 - 300 *C, where the specific contact resistances are typically in the 10-2 K2-cm2 range. The best contacts for W and WSiX are obtained after 700 *C annealing for periods of 30- 120 sees. The formation of &WzN interracial phases appear to be important in determining the contact quality.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 1377
- Report Number(s):
- SAND98-2301J; ON: DE00001377
- Journal Information:
- Journal of Vacuum Science and Technology A, Journal Name: Journal of Vacuum Science and Technology A
- Country of Publication:
- United States
- Language:
- English
Similar Records
High temperature stable WSi{sub x} ohmic contacts on GaN
High temperature stable W and WSi{sub x} ohmic contacts on GaN and InGaN