Small Specimen Data from a High Temperature HFIR Irradiation Experiment
- ORNL
The HTV capsule is a High Flux Isotope Reactor (HFIR) target-rod capsule designed to operate at very high temperatures. The graphite containing section of the capsule (in core) is approximately 18 inches (457.2 mm) long and is separated into eight temperature zones. The specimen diameters within each zone are set to achieve the desired gas gap and hence design temperature (900 C, 1200 C or 1500 C). The capsule has five zones containing 0.400 inch (10.16 mm) diameter specimens, two zones containing 0.350 inch (8.89 mm) diameter specimens and one zone containing 0.300 inch (7.62 mm) diameter specimens. The zones have been distributed within the experiment to optimize the gamma heating from the HFIR core as well as minimize the axial heat flow in the capsule. Consequently, there are two 900 C zones, three 1200 C zones, and three 1500 C zones within the HTV capsule. Each zone contains nine specimens 0.210 0.002 inches (5.334 mm) in length. The capsule will be irradiated to a peak dose of 3.17 displacements per atom. The HTV specimens include samples of the following graphite grades: SGL Carbon s NBG-17 and NBG-18, GrafTech s PCEA, Toyo Tanso s IG-110, Mersen s 2114 and the reference grade H-451 (SGL Carbon). As part of the pre-irradiation program the specimens were characterized using ASTM Standards C559 for bulk density, and ASTM C769 for approximate Young s modulus from the sonic velocity. The probe frequency used for the determination of time of flight of the ultrasonic signal was 2.25 MHz. Marked volume (specimen diameter) effects were noted for both bulk density (increased with increasing specimen volume or diameter) and Dynamic Young s modulus (decreased with increasing specimen volume or diameter). These trends are extended by adding the property vs. diameter data for unirradiated AGC-1 creep specimens (nominally 12.5 mm-diameter x 25.4 mm-length). The relatively large reduction in Dynamic Young s Modulus was surprising given the trend for increasing density with increasing volume. The graphite-filler particle size was noted to be influential in the volume dependency data, with finer grained graphites showing the least specimen volume/diameter effect. Here the volume dependency trends are discussed in terms of the graphite s filler-particle size and texture.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). High Flux Isotope Reactor (HFIR)
- Sponsoring Organization:
- Work for Others (WFO)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1163151
- Resource Relation:
- Conference: ASTM STP1578: Symposium on Graphite Testing for Nuclear Applications: The Significance of Test Specimen Volume and Geometry and the Statistical Significance of Test Specimen Population, Seattle, WA, USA, 20130919, 20130920
- Country of Publication:
- United States
- Language:
- English
Similar Records
The Effect of Neutron Irradiation Damage on the Properties of Grade NBG-10 Graphite
AGC-1 Sister Specimen Testing Data Report