Measurements of BET Surface Area on Silica Nanosprings
Nitrogen adsorption desorption isotherm for Silica nanosprings (GoNano2) samples deposited on substrate. The isotherm was obtained at 77 K using liquid N2 bath. The area of the substrate is 16 cm2. The amount of the sample is 0.44 mg/cm2. Amount of silica nanosprings= 7.04 mg. There is no indication of substantial micro or mesoporosity in the sample based on the nature of the isotherm. Eleven point BET surface area was measured. Nine points plotted. Goodness if fit R= 0.9992. BET surface area for silica nanosprings= 262 cm2/g
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1134530
- Report Number(s):
- PNNL-17648
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetic properties of mesoporous cobalt-silica-alumina ternary mixed oxides
Measurements of water vapor adsorption on the Geysers rocks
Synthesis and characterization of high-surface-area millimeter-sized silica beads with hierarchical multi-modal pore structure by the addition of agar
Journal Article
·
Fri Feb 15 00:00:00 EST 2013
· Journal of Solid State Chemistry
·
OSTI ID:1134530
Measurements of water vapor adsorption on the Geysers rocks
Conference
·
Wed Jan 24 00:00:00 EST 1996
·
OSTI ID:1134530
+1 more
Synthesis and characterization of high-surface-area millimeter-sized silica beads with hierarchical multi-modal pore structure by the addition of agar
Journal Article
·
Tue Apr 01 00:00:00 EDT 2014
· Materials Characterization
·
OSTI ID:1134530
+1 more