Friction and wear behavior of in-situ reinforced silicon nitride. Final report
Specimens of in-situ-reinforced silicon nitride (ISRSH) have been wear tested in lubricated, reciprocating, sliding motion against a silicon nitride counterface. Only mild wear of the ISRSN was observed at contact pressures up to 4.8 GPa at an average sliding velocity of 0.3 m/s. At 0.6 m/s, a wear mode transition was observed in ISRSN at 4.2 - 4.4 GPa. In comparison, the wear mode transition in silicon carbide whisker reinforced silicon nitride at both velocities was evident at about 2.2 - 2.4 GPa. Scanning electron microscopy of the ISRSN wear surfaces revealed the presence of a 40 pm thick debris layer on the mild wear tracks. The ISRSN wear mode transition response indicated a potential for an improved wear resistance in this material as compared to whisker reinforced silicon nitride.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-84OR21400
- OSTI ID:
- 110747
- Report Number(s):
- DOE/OR/21400-T480; ON: DE96000759; TRN: 95:007275
- Resource Relation:
- Other Information: PBD: [1995]
- Country of Publication:
- United States
- Language:
- English
Similar Records
The friction and wear of lubricated Si sub 3 N sub 4 /SiC(w) composites
Effects of surface grinding conditions on the reciprocating friction and wear behavior of silicon nitride