Laser beam welding of any metal.
The effect of a metal's thermophysical properties on its weldability are examined. The thermal conductivity, melting point, absorptivity and thermal diffusivity of the metal and the laser beam focused diameter and welding speed influence the minimum beam irradiance required for melting and welding. Beam diameter, surface tension and viscosity of the molten metal affect weld pool stability and weld quality. Lower surface tension and viscosity increases weld pool instability. With larger beam diameters causing wider welds, dropout also increases. Effects of focused beam diameter and joint fitup on weldability are also examined. Small beam diameters are sensitive to beam coupling problems in relation to fitup precision in addition to beam alignment to the seam. Welding parameters for mitigating weld pool instability and increasing weld quality are derived from the above considerations. Guidelines are presented for the tailoring of welding parameters to achieve good welds. Weldability problems can also be anticipated from the properties of a metal.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 10807
- Report Number(s):
- ANL/TD/CP-96467; TRN: AH200127%%354
- Resource Relation:
- Conference: 17th International Congress on Applications of Lasers and Electro-Optics (ICALEO '98), Orlando, FL (US), 11/16/1998--11/19/1998; Other Information: PBD: 1 Oct 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Laser beam welding of AZ31B-H24 magnesium alloy.
Verification of a dimensionless parameter model for laser beam welding