Surface area and chemical reactivity characteristics of uranium metal corrosion products.
Conference
·
OSTI ID:10646
The results of an initial characterization of hydride-containing corrosion products from uranium metal Zero Power Physics Reactor (ZPPR) fuel plates are presented. Sorption analyses using the BET method with a Kr adsorbate were performed to measure the specific areas of corrosion product samples. The specific surface areas of the corrosion products varied from 0.66 to 1.01 m{sup 2}/g. The reactivity of the products in Ar-9%O{sub 2} and Ar-20%O{sub 2} were measured at temperatures between 35 C and 150 C using a thermo-gravimetric analyzer. Ignition of the products occurred at temperatures of 150 C and above. The oxidation rates below ignition were comparable to rates observed for uranium metal.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 10646
- Report Number(s):
- ANL/ED/CP-95647; TRN: US0103788
- Resource Relation:
- Conference: Waste Management '98, Tucson, AZ (US), 03/01/1998--03/05/1998; Other Information: PBD: 17 Feb 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of uranium corrosion products involved in the March 13, 1998 fuel manufacturing facility pyrophoric event.
Oxidation of ZPPR fuel corrosion products : National Spent Nuclear Fuel program FY 1999 final report.
Oxidation kinetics of reaction products formed in uranium metal corrosion.
Technical Report
·
Mon Apr 26 00:00:00 EDT 1999
·
OSTI ID:10646
Oxidation of ZPPR fuel corrosion products : National Spent Nuclear Fuel program FY 1999 final report.
Technical Report
·
Wed Nov 10 00:00:00 EST 1999
·
OSTI ID:10646
Oxidation kinetics of reaction products formed in uranium metal corrosion.
Conference
·
Wed Apr 22 00:00:00 EDT 1998
·
OSTI ID:10646