Preliminary Test Results from 650 MHz Single Cell Medium Beta Cavities for Project X
We have fabricated two single cell 650 MHz {beta}=0.61 cavities of a JLab design, which possibly can be used for the proposed Project X proton linac application. Both cavities were manufactured at JLab from RRR>250 niobium sheet of 4 mm thickness using standard techniques such as deep drawing, electron beam welding, buffered chemical polishing, hydrogen degassing heat treatment, high pressure ultrapure water rinsing and clean room assembly. Initially cavity no. 1 was -- after final surface treatment by buffered chemical polishing (BCP) -- measured without any provisions for stiffening. As expected, the pressure sensitivity and the Lorentz Force detuning coefficients were relatively high; however, the RF performance was very encouraging: the cavity exhibited a Q-value > 10{sup 11} at 1.6K, corresponding to a residual resistance of < 1.5 n{Omega} The initial gradient was limited to E{sub acc} ~ 18 MV/m, limited by field emission. In a subsequent test, the cavity was re-rinsed and stiffened up, resulting in a somewhat improved mechanical behavior, but no improvement in rf performance. The second cavity was also tested twice, before and after low temperature baking. The results from all tests are reported in this contribution.
- Research Organization:
- Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- AC05-06OR23177
- OSTI ID:
- 1057759
- Report Number(s):
- JLAB-ACC-11-1448; DOE/OR/23177-1854; TRN: US1300397
- Resource Relation:
- Conference: SRF 2011 (RF Superconductivity), Chicago, IL (United States), 25-29 Jul 2011
- Country of Publication:
- United States
- Language:
- English
Similar Records
A selection of high gradient cavity experiments
Advanced surface cleaning methods: three years of experience with high pressure ultrapure water rinsing of superconducting cavaties