Physics-Based Stress Corrosion Cracking Component Reliability Model cast in an R7-Compatible Cumulative Damage Framework
This is a working report drafted under the Risk-Informed Safety Margin Characterization pathway of the Light Water Reactor Sustainability Program, describing statistical models of passives component reliabilities.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1024549
- Report Number(s):
- PNNL-20596; 830403000; TRN: US1104784
- Country of Publication:
- United States
- Language:
- English
Similar Records
Physics-Based Multi-State Models of Passive Component Degradation for the R7 Reactor Simulation Environment
Multi-State Physics Models of Aging Passive Components in Probabilistic Risk Assessment
Proof-of-Concept Demonstrations for Computation-Based Human Reliability Analysis. Modeling Operator Performance During Flooding Scenarios
Conference
·
Mon Jun 25 00:00:00 EDT 2012
·
OSTI ID:1024549
+1 more
Multi-State Physics Models of Aging Passive Components in Probabilistic Risk Assessment
Conference
·
Sun Mar 13 00:00:00 EST 2011
·
OSTI ID:1024549
+2 more
Proof-of-Concept Demonstrations for Computation-Based Human Reliability Analysis. Modeling Operator Performance During Flooding Scenarios
Technical Report
·
Tue Sep 01 00:00:00 EDT 2015
·
OSTI ID:1024549
+2 more
Related Subjects
22 GENERAL STUDIES OF NUCLEAR REACTORS
ACCIDENTS
AGING
ALLOYS
BOUNDARY CONDITIONS
COOLANTS
DECISION MAKING
LOSS OF COOLANT
MANAGEMENT
REACTOR OPERATION
RELIABILITY
REPAIR
RISK ASSESSMENT
SAFETY MARGINS
SIMULATION
STATISTICAL MODELS
STRESS CORROSION
WATER
INEEL
Risk
passive components
materials reliability
stress corrosion cracking
ACCIDENTS
AGING
ALLOYS
BOUNDARY CONDITIONS
COOLANTS
DECISION MAKING
LOSS OF COOLANT
MANAGEMENT
REACTOR OPERATION
RELIABILITY
REPAIR
RISK ASSESSMENT
SAFETY MARGINS
SIMULATION
STATISTICAL MODELS
STRESS CORROSION
WATER
INEEL
Risk
passive components
materials reliability
stress corrosion cracking