Creep properties of PWC-11 base metal and weldments as affected by heat treatment
- Lewis Research Center, Cleveland, OH (United States)
In a preliminary study using single specimens for each condition, PWC-11 (a niobium-base alloy with a nominal composition of Nb-1%Zr-0.1%C) was creep tested at 1350 K and 40 MPa. Base metal specimens and specimens with transverse electrode beam welds were tested with and without a 1000 hr, 1350 K aging treatment prior to testing. In the annealed condition (1 hr at 1755 K + 2 hr at 1475 K), the base metal exhibited superior creep strength compared to the aged condition, reaching 1 percent strain in 3480 hr. A 1000 hr, 1350 K aging treatment prior to creep testing had a severe detrimental effect on creep strength of the base metal and transverse electron beam weldments, reducing the time to attain 1 percent strain by an order of magnitude. Extrapolated temperature compensated creep rates indicate that the present heat of PWC-11 may be four times as creep resistance as similarly tested Nb-1%Zr. The extrapolated stress to achieve 1 percent creep strain in 7 yr at 1350 K is 0.6 MPa for annealed Nb-1%Zr and 2.8 MPa for annealed and aged PWC-11 base metal with and without a transverse electron beam weld.
- Research Organization:
- National Aeronautics and Space Administration, Cleveland, OH (United States). Lewis Research Center
- Sponsoring Organization:
- National Aeronautics and Space Administration, Washington, DC (United States); USDOE, Washington, DC (United States)
- DOE Contract Number:
- AI03-86SF16310
- OSTI ID:
- 10181379
- Report Number(s):
- NASA-TM-88842; CONF-8603231-1; ON: DE94051240; TRN: 94:008342
- Resource Relation:
- Conference: TMS-AIME annual meeting on alternate alloying for environmental resistance,New Orleans, LA (United States),2-6 Mar 1986; Other Information: PBD: [1994]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Creep behavior of the niobium alloy PWC-11. [Nb - 1 Zr - 0. 1 C]
The effect of electron beam welding on the creep rupture properties of a Nb-Zr-C alloy. [Nb-1Zr-0. 1C (PWC-11)]
Related Subjects
22 GENERAL STUDIES OF NUCLEAR REACTORS
36 MATERIALS SCIENCE
REACTOR COMPONENTS
CREEP
WELDED JOINTS
NIOBIUM ALLOYS
HEAT TREATMENTS
SPACE POWER REACTORS
NESDPS Office of Nuclear Energy Space and Defense Power Systems
210600
220200
360103
POWER REACTORS, MOBILE, PROPULSION, PACKAGE, AND TRANSPORTABLE
COMPONENTS AND ACCESSORIES
MECHANICAL PROPERTIES