The microstructure and morphology of carbon black: A study using small angle neutron scattering and contrast variation
- Los Alamos National Lab., NM (United States)
- Sid Richardson Carbon Co., Fort Worth, TX (United States)
This is a study of the microstructure of particles of an experimental high surface area carbon black (HSA) and of the morphology of the particle aggregates using small-angle neutron scattering and the method of contrast variation. Contrast variation was effected by studying suspensions of the carbon black in cyclohexane containing different fractions of deuterocyclohexane. We find that the approximately 29 nm diameter HSA particles are arranged as small, linear aggregates with average aggregation number between 4 and 6. The structure averaged over the particle population is best represented by a prolate ellipsoid of revolution with semi axes 14.5 and 76.4 nm. The surface of the aggregates appears smooth over length scales longer than 1 nm, which places an upper limit on the surface roughness observed by other methods. The intemal structure of the aggregates is described by a shell-core model, with the shell density being consistent with a graphitic structure and the core being of lower density, more like amorphous carbon. Some fraction of the core volume (0.1 to 0.2) is taken up by voids that are not accessible to the solvent. An estimate of the shell thickness gives 1 to 2 nm along the ellipsoid minor axis and 6 to 10 nm along the major axis. The particles of the aggregate appear to be fused so that the less dense amorphous core is continuous through the inner parts of the aggregate. The information that can be obtained on the internal structure using contrast variation is limited by nonheterogeneity in the chemical composition of carbon black aggregates.
- Research Organization:
- Los Alamos National Lab., NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 10139285
- Report Number(s):
- LA-UR-94-818; CONF-9404124-1; ON: DE94009315; TRN: 94:007507
- Resource Relation:
- Conference: American Chemical Society (ACS) conference,Chicago, IL (United States),Apr 1994; Other Information: PBD: [1994]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Variation of solvent scattering-length density small-angle neutron scattering as a means of determining structure of composite materials
The structure of carbon black and its composites with elastomers: A study using neutron scattering