RESULTS OF THE EXAMINATION OF ELECTROCHEMICAL NOISE PROBE SPECIMENS REMOVED FROM TANK 241-AN-107 JUNE 2010
An Integrated Multi-function Corrosion Probe (IMCP) was installed in Tank 241-AN-107 on September 20, 2006. A portion of the probe was retrieved on June 8, 2010 and the sections holding the detectors were delivered to the 222-S Laboratory for analysis. The examination and disassembly of the probe sections encountered a number of challenges. However, disassembly and relevant analyses were successfully completed. The following summarizes our observations. Brittle failure of the fiberglass probe in the middle of detector 2 resulted in the recovery of only three vapor space C-rings and six supernatant bullet specimens. The design of the bullets and how they were attached to the probe made the recovery of the components more difficult. The use of glue/epoxy on the bullets and the attachment of the flat bottom of the bullets to the curved surface of the fiberglass probe body meant that weight loss on cleaning and surface area of the specimens could not be determined with acceptable accuracy. Macrophotography of all specimens reveals that corrosion was slight in the vapor space and extremely slight in the supernatant. The one pre-cracked C-ring recovered from the vapor space still had the stress bulge visible on the polished surface, indicating that crack propagation had not occurred in the tank. No photographs were taken of the C-ring before deployment. No further analysis was conducted on this specimen. A detailed discussion and photographic documentation are provided in this report.
- Research Organization:
- Hanford Site (HNF), Richland, WA (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Environmental Management (EM)
- DOE Contract Number:
- DE-AC27-08RV14800
- OSTI ID:
- 1000336
- Report Number(s):
- LAB-RPT-10-00011 Rev 0; TRN: US1100093
- Country of Publication:
- United States
- Language:
- English