Fabrication of Monolithic RERTR Fuels by Hot Isostatic Pressing
The RERTR (Reduced Enrichment for Research and Test Reactors) Program is developing advanced nuclear fuels for high-power test reactors. Monolithic fuel design provides higher uranium loading than that of the traditional dispersion fuel design. Hot isostatic pressing is a promising process for low-cost batch fabrication of monolithic RERTR fuel plates for these high-power reactors. Bonding U Mo fuel foil and 6061 Al cladding by hot isostatic press bonding was successfully developed at Idaho National Laboratory. Due to the relatively high processing temperature, the interaction between fuel meat and aluminum cladding is a concern. Two different methods were employed to mitigate this effect: (1) a diffusion barrier and (2) a doping addition to the interface. Both types of fuel plates have been fabricated by hot isostatic press bonding. Preliminary results show that the direct fuel/cladding interaction during the bonding process was eliminated by introducing a thin zirconium diffusion barrier layer between the fuel and the cladding. Fuel plates were also produced and characterized with a silicon-rich interlayer between fuel and cladding. This paper reports the recent progress of this developmental effort and identifies the areas that need further attention.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- DOE - NE
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 992255
- Report Number(s):
- INL/JOU-09-16617; NUTYBB; TRN: US1007709
- Journal Information:
- Nuclear Technology, Vol. 172, Issue 2; ISSN 0029-5450
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural Characteristics of HIP-bonded Monolithic Nuclear Fuels with a Diffusion Barrier
Growth kinetics and microstructural evolution during hot isostatic pressing of U-10 wt.% Mo monolithic fuel plate in AA6061 cladding with Zr diffusion barrier