High strength zirconia ceramics from green body preforms
Conference
·
OSTI ID:99149
- Tioxide Specialties Ltd., Billingham (United Kingdom)
High strength zirconia ceramic articles ({approx}1.3GPa) have been manufactured by subjecting a mixture of zirconia powder, a binder, a plasticiser and a solvent to high shear mixing to reduce the size of flaw forming powder agglomerates. A flexible green body preform was produced that was further extruded or calendered to the final shape, e.g. flat plates and coil springs, prior to sintering to full density.
- OSTI ID:
- 99149
- Report Number(s):
- CONF-940911-; TRN: 95:005310-0039
- Resource Relation:
- Conference: 5. international conference on ceramic processing science and technology, Friedrichshafen (Germany), 11-14 Sep 1994; Other Information: PBD: 1995; Related Information: Is Part Of Ceramic transactions: Ceramic processing science and technology. Volume 51; Hausner, H.; Messing, G.L.; Hirano, Shin-ichi [eds.]; PB: 835 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Colloidal processing of coprecipitated alumina:chromia/zirconia
Application of NDE methods to green ceramics: initial results
Superplastic forging nitride ceramics
Miscellaneous
·
Sun Jan 01 00:00:00 EST 1989
·
OSTI ID:99149
Application of NDE methods to green ceramics: initial results
Conference
·
Sat Jan 01 00:00:00 EST 1983
·
OSTI ID:99149
+4 more
Superplastic forging nitride ceramics
Patent
·
Tue Mar 22 00:00:00 EST 1988
·
OSTI ID:99149