In-situ observation of dynamic recrystallization in the bulk of zirconium alloy.
Dynamic recrystallization and related effects have been followed in situ and in real time while a metal undergoes rapid thermo-mechanical processing. Statistics and orientation correlations of embedded/bulk material grains were deduced from two-dimensional X-ray diffraction patterns and give deep insight into the formation of the microstructure. Applications are relevant in materials design, simulation, and in geological systems.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC); Australian Synchrotron Research Program
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 985631
- Report Number(s):
- ANL/XSD/JA-64031; TRN: US201016%%2082
- Journal Information:
- Adv. Eng. Mater., Vol. 11, Issue 8 ; Aug. 2009
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
In situ observation of dynamic recrystallization in five-nine aluminum by a transmission Laue method
Multiscale in-situ characterization of static recrystallization using dark-field X-ray microscopy and high-resolution X-ray diffraction
Effect of initial orientation on dynamic recrystallization of a zirconium alloy during hot deformation
Journal Article
·
Tue Feb 15 00:00:00 EST 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:985631
Multiscale in-situ characterization of static recrystallization using dark-field X-ray microscopy and high-resolution X-ray diffraction
Journal Article
·
Thu Mar 14 00:00:00 EDT 2024
· Scientific Reports
·
OSTI ID:985631
+3 more
Effect of initial orientation on dynamic recrystallization of a zirconium alloy during hot deformation
Journal Article
·
Thu Nov 15 00:00:00 EST 2018
· Materials Characterization
·
OSTI ID:985631
+4 more