Electrolyte additive to improve performance of MCMB LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} Li-ion cell.
The electrolyte additive, 3,9-divinyl-2,4,8,10-tetraoxaspiro[5,5] undecane (TOS), was investigated as a means to improve the life of mesocarbon microbead (MCMB)/Li1.1[Ni1/3Co1/3Mn1/3]0.9O2 (NCM) cells for high-power applications. With the addition of an appropriate amount of TOS (no more than 1 wt%) to MCMB/NCM cells, the capacity retention was significantly improved at 55 C compared with cells containing pristine electrolyte. Aging tests at 55 C indicated that the capacity retention of the negative electrode had benefited as a result of the formation of a stable passivation film at the surface of the carbon electrode due to TOS reduction. Electrochemical impedance spectroscopy showed that a TOS addition of more than 0.5 wt% increased the cell interfacial impedance. Differential scanning calorimetry showed that the thermal stability of lithiated MCMB was also improved with the TOS addition.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- EE
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 984300
- Report Number(s):
- ANL/CSE/JA-66834; TRN: US201015%%955
- Journal Information:
- J. Power Sources, Vol. 195, Issue 19 ; Oct. 1, 2010
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Lithium tetrafluoro oxalato phosphate as electrolyte additive for lithium-ion cells.
Effect of low-temperature conditions on passive layer growth in Li intercalation materials: In situ impedance study