In-Situ Observations of Sigma Phase Dissolution in 2205 Duplex Stainless Steel Using Synchrotron X-Ray Diffraction
Journal Article
·
· Materials Science and Engineering A
- Lawrence Livermore National Laboratory (LLNL)
- ORNL
Synchrotron radiation was used to directly observe the transformation of ferrite, austenite and sigma phases during heating and cooling of 2205 duplex stainless steel. Sigma formed during the initial stages of heating, dissolved as the temperature was increased, and reformed on cooling. The dissolution temperature of sigma was measured to be 985 2.8 C at a heating rate of 0.25 C/s, and the kinetics of sigma formation at 850 Cwas determined to be slower after dissolving at 1000 C than before.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 962983
- Journal Information:
- Materials Science and Engineering A, Vol. 459, Issue 1-2
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-Situ Observations of Sigma Phase Dissolution in 2205 Duplex Stainless Steel using Synchrotron X-Ray Diffraction
Direct Observations of Sigma Phase Growth and Dissolution in 2205 Duplex Stainless Steel
Direct observations of sigma phase growth and dissolution in 2205 duplex stainless steel
Journal Article
·
Tue Aug 08 00:00:00 EDT 2006
· Materials Science and Engineering A, n/a, n/a, November 30, 1999, n/a
·
OSTI ID:962983
Direct Observations of Sigma Phase Growth and Dissolution in 2205 Duplex Stainless Steel
Conference
·
Tue Jun 14 00:00:00 EDT 2005
·
OSTI ID:962983
+1 more
Direct observations of sigma phase growth and dissolution in 2205 duplex stainless steel
Conference
·
Wed Oct 10 00:00:00 EDT 2007
·
OSTI ID:962983
+1 more